S-LEC Types and General Characteristics
Form
Packaging | 20kg/Craft plapr bag |
---|---|
Color | White (powder) |
Specific gravity | from 0.20 to 0.40 |
Types of S-LEC B, K and General Characteristics
Grade | Type | Volatiles (%) |
Mw ×104 |
Viscosity | Hydroxyl content |
Acetyl content |
Acetal content |
Tg (℃) |
||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
5wt% | 10wt% | (mol%) | (wt%) | (mol%) | (wt%) | (mol%) | (wt%) | |||||
(mPa・s) |
Low-Molecular-Weight Type | ||||||||||||
BL-10 | P | 3 or less | 1.5 | - | 9~15 | Approx. 28 | Approx. 19 | 3 or less | 4 or less | Approx. 70 | Approx. 78 | 67 |
---|---|---|---|---|---|---|---|---|---|---|---|---|
BL-1 | P | 3 or less | 1.9 | - | 10~30 | Approx. 36 | Approx. 26 | 3 or less | 4 or less | Approx. 63 | Approx. 73 | 70 |
BL-1H | P | 3 or less | 2.0 | - | 10~30 | Approx. 30 | Approx. 21 | 3 or less | 4 or less | Approx. 69 | Approx. 78 | 68 |
BL-S | P | 3 or less | 2.3 | - | 10~30 | Approx. 23 | Approx. 16 | 4~6 | 5~7 | Approx. 72 | Approx. 78 | 66 |
BL-2H | P | 3 or less | 2.8 | - | 25~55 | Approx. 30 | Approx. 21 | 3 or less | 4 or less | Approx. 69 | Approx. 78 | 70 |
BL-5Z | Z | 3 or less | 3.2 | - | 30~50 | Approx. 21 | Approx. 14 | 3 or less | 4 or less | Approx. 77 | Approx. 83 | 67 |
BL-7Z | Z | 3 or less | 3.9 | - | 50~90 | Approx. 30 | Approx. 21 | 3 or less | 4 or less | Approx. 69 | Approx. 78 | 71 |
Medium-Molecular-Weight Type | ||||||||||||
BM-1 | P | 3 or less | 4.0 | - | 60~100 | Approx. 34 | Approx. 24 | 3 or less | 4 or less | Approx. 65 | Approx. 75 | 72 |
BM-S(Z) | P/Z | 3 or less | 5.5 | - | 80~150 | Approx. 23 | Approx. 16 | 4~6 | 5~7 | Approx. 72 | Approx. 78 | 67 |
BM-2(Z) | P/Z | 3 or less | 5.2 | - | 100~170 | Approx. 30 | Approx. 21 | 3 or less | 4 or less | Approx. 69 | Approx. 78 | 71 |
BM-SHZ | Z | 3 or less | 5.8 | - | 110~190 | Approx. 23 | Approx. 16 | 3 or less | 4 or less | Approx. 77 | Approx. 83 | 68 |
BM-5 | P | 3 or less | 5.6 | - | 140~220 | Approx. 34 | Approx. 24 | 3 or less | 4 or less | Approx. 65 | Approx. 75 | 73 |
High-Molecular-Weight Type | ||||||||||||
BH-S | P | 3 or less | 6.6 | 20~40 | - | Approx. 23 | Approx. 16 | 4~6 | 5~7 | Approx. 72 | Approx. 78 | 67 |
BH-A | P | 3 or less | 11.5 | 35~65 | - | Approx. 27 | Approx. 18 | 11~15 | 15~19 | Approx. 60 | Approx. 65 | 65 |
BH-6 | P | 3 or less | 9.2 | 40~90 | - | Approx. 30 | Approx. 21 | 3 or less | 4 or less | Approx. 69 | Approx. 78 | 73 |
BH-3(Z) | P/Z | 3 or less | 11.0 | 60~120 | - | Approx. 34 | Approx. 24 | 3 or less | 4 or less | Approx. 65 | Approx. 75 | 74 |
Heat-Resistant Type | ||||||||||||
BX-L | P | 3 or less | 1.8 | - | 10~30 | Approx. 32 | Approx. 25 | 3 or less | 4 or less | Approx. 67 | Approx. 74 | 80 |
BX-1 | P | 3 or less | 10.0 | 70~140 | - | Approx. 27 | Approx. 21 | 3 or less | 4 or less | Approx. 72 | Approx. 78 | 95 |
BX-5(Z) | P/Z | 3 or less | 13.0 | 130~200 | - | Approx. 27 | Approx. 21 | 3 or less | 4 or less | Approx. 72 | Approx. 78 | 92 |
High-Heat-Resistant Type | ||||||||||||
KS-10 | P | 3 or less | 1.7 | - | 10~30 | Approx. 25 | Approx. 20 | 3 or less | 4 or less | Approx. 74 | Approx. 78 | 105 |
KS-1 | P | 3 or less | 2.7 | - | 65~95 | Approx. 25 | Approx. 20 | 3 or less | 4 or less | Approx. 74 | Approx. 78 | 107 |
KS-6Z | Z | 3 or less | 10.8 | 110~170 | - | Approx. 25 | Approx. 20 | 3 or less | 4 or less | Approx. 74 | Approx. 78 | 113 |
KS-5Z | Z | 3 or less | 13.0 | 210~270 | - | Approx. 25 | Approx. 20 | 3 or less | 4 or less | Approx. 74 | Approx. 78 | 113 |
Note:
Shape: P = Particulate, Z = Granule
Viscosity: Ethanol/toluene = 1/1 solution (Measurement instrument: BM Type rotary viscometer/Measurement temperature: 20°C)
* The values are not above specifications.
Shape: P = Particulate, Z = Granule
Viscosity: Ethanol/toluene = 1/1 solution (Measurement instrument: BM Type rotary viscometer/Measurement temperature: 20°C)
* The values are not above specifications.
S-LEC K(KX)
Grade | Degree of polymerization |
Solids Content (wt%) |
Viscosity (mPa・s) |
Degree of acetalization (mol%) |
pH (ppm) |
Solvent |
---|---|---|---|---|---|---|
KX-1 | Approx.3,500 | 8±2 | 10,000 ±6,000 |
8±2 | 6±2 | IPA/Water |
KX-5 | Approx.2,000 | 8±2 | 3,000 ±1,500 |
9±2 | 6±2 | IPA/Water |
S-LEC K(KW)
Grade | Degree of polymerization |
Solids Content (wt%) |
Viscosity (mPa・s) |
曇点 (℃) |
Degree of acetalization (mol%) |
pH (ppm) |
Solvent |
---|---|---|---|---|---|---|---|
KW-M | Approx.600 | 20±2 | 2,000 ±1,000 |
50±5 | 24±3 | 5±1 | Water |
KW-10 | Approx.600 | 24±2 | 3,500 ±1,500 |
55±5 | 9±2 | 5±1 | Water |
* All values shown to table mentioned above are not specification limit.